變(bian)壓器由初級線(xian)圈、次級線(xian)圈和鐵芯(磁芯)構成，利(li)用電(dian)磁感應原理改變(bian)交(jiao)流電(dian)壓的一(yi)種裝置。常見問題主(zhu)要(yao)有以下(xia)幾點(dian)：

       首先，因(yin)繞(rao)線飽滿(man)造(zao)成膠(jiao)心(xin)(xin)(xin)變形,插片(pian)(pian)(pian)后鐵(tie)心(xin)(xin)(xin)E片(pian)(pian)(pian)與I片(pian)(pian)(pian)之間有氣隙(xi),引(yin)起空(kong)(kong)載電流(liu)(liu)大,此時繞(rao)好線的膠(jiao)心(xin)(xin)(xin)整形即可；而EI-76鐵(tie)心(xin)(xin)(xin)片(pian)(pian)(pian)規定空(kong)(kong)載電流(liu)(liu)不大于57ma實際達到67ma，原因(yin)是鐵(tie)心(xin)(xin)(xin)片(pian)(pian)(pian)插得緊(jin),使鐵(tie)心(xin)(xin)(xin)產生應力,將鐵(tie)芯(xin)片(pian)(pian)(pian)取出一片(pian)(pian)(pian)空(kong)(kong)載電流(liu)(liu)即達到54ma。

       其次(ci)，如果空(kong)載電(dian)流大，更(geng)換鐵(tie)芯(xin)片(pian)不合格，可以更(geng)換為高性(xing)能鐵(tie)芯(xin)片(pian)。如果空(kong)載電(dian)流比(bi)原來小，溫度(du)上升超差，H50材料的空(kong)載電(dian)流小，鐵(tie)損失大。

       再次，EI-66鐵(tie)心變(bian)壓(ya)器(qi)，設計(ji)磁通密度為1.3 T，測空載電流(liu)為135 ma，且有嗡(weng)嗡(weng)聲，此時需要(yao)更換鐵(tie)心片(pian)；如果搖片(pian)困難，且鐵(tie)心片(pian)表面有劃(hua)痕，這是由于(yu)在放置鐵(tie)芯片(pian)的(de)爐架上(shang)焊接時，未對焊渣(zha)進行(xing)處理，高溫下焊渣(zha)破裂所致。

       第四，浸(jin)(jin)漬(zi)前變(bian)壓(ya)器端(duan)面無銹蝕，浸(jin)(jin)漬(zi)后(hou)端(duan)面有(you)銹蝕；主要是手汗造成的，因為浸(jin)(jin)漬(zi)漆(qi)層(ceng)很(hen)薄，有(you)針孔，浸(jin)(jin)泡放置一(yi)段時(shi)間后(hou)會(hui)產生銹跡(ji)；所以夏天(tian)戴手套可避(bi)免。此外，變(bian)壓(ya)器含(han)浸(jin)(jin)后(hou)，空載電流(liu)增加很(hen)多，其原因是涂上了環(huan)氧(yang)樹脂，含(han)浸(jin)(jin)后(hou)收縮應力較大，改進(jin)措施是改變(bian)涂料粘度，或(huo)改用其它涂料。

       第五，變壓器在(zai)試驗(yan)過程(cheng)中嗡嗡作(zuo)響:這是(shi)由于(yu)芯板E的厚(hou)度(du)與芯板I的厚(hou)度(du)不(bu)一致(zhi)造成的，所以解(jie)決(jue)辦法是(shi)換板或增加浸漬工序；厚(hou)度(du)要(yao)求(qiu):將(jiang)芯塊放在(zai)平板上(shang)，用測(ce)厚(hou)儀(yi)測(ce)量。板形要(yao)求(qiu)小于(yu)0.25毫米。